In vitro analysis of durability of S-PRG filler-containing composite crowns for primary molar restoration.

OBJECTIVE: To evaluate the reliability, maximum principal stress, shear stress, and crack initiation of a computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite (RC) incorporating surface pre-reacted glass (S-PRG) filler for primary molar teeth. METHODS: Mandibular primary molar crowns fabricated by experimental (EB) or commercially available CAD/CAM RCs (HC) were prepared and cemented to a resinous abutment tooth using an adhesive resin cement (Cem) or a conventional glass-ionomer cement (CX). These specimens were subjected to a single compressive test (n = 5/each) and the step-stress accelerated life testing (SSALT) (n = 12/each). Data was evaluated using Weibull analyses and reliability was calculated. Afterwards, the maximum principal stress and crack initiation point of each crown was analyzed by finite element analysis. To evaluate bonding of EB and HC to dentin, microtensile bond strength (µTBS) testing was conducted using primary molar teeth (n = 10/each). RESULTS: There was no significant difference between the fracture loads of EB and HC for either cement (p > 0.05). The fracture loads of EB-CX and HC-CX were significantly lower than EB-Cem and HC-Cem (p < 0.05). The reliability at 600 N for EB-Cem was greater than that for EB-CX, HC-Cem, and HC-CX. The maximum principal stress concentrated on EB was lower than that on HC. The shear stress concentrated in the cement layer for EB-CX was higher than that for HC-CX. There was no significant difference among the µTBSs of EB-Cem, EB-CX, HC-Cem, and HC-CX (p > 0.05). SIGNIFICANCE: The crowns fabricated with the experimental CAD/CAM RC incorporating S-PRG filler yielded greater fracture loads and reliability than the crowns manufactured with commercially available CAD/CAM RC regardless of the luting materials. These findings suggest that the experimental CAD/CAM RC crown may be clinically useful for the restoration of primary molars.

Bone regeneration at extraction sockets filled with leukocyte-platelet-richfibrin: An experimental pre-clinical study

Background: We aimed to histomorphometrically evaluate the effects of Leucocyte-Platelet-Rich Fibrin (L-PRF),with and without the combination of a bone grafting material, for alveolar ridge preservation using an in vivocanine model.Material and Methods: Seven dogs (Female Beagles, ~18-month-old) were acquired for the study. L-PRF wasprepared from each individual animal by drawing venous blood and spinning them through a centrifuge at 408RCF-clot (IntrasSpin, Intra-Lock, Boca Raton, FL). L-PRF membranes were obtained from XPression fabrication kit (Biohorizons Implant Systems, Inc., AL, USA). A split mouth approach was adopted with the first molarmesial and distal socket defects treated in an interpolated fashion of the following study groups: 1) Empty socket (negative control); 2) OSS filled defect 3) L-PRF membrane; and 4) Mix of Bio-Oss® with L-PRF. After six weeks,samples were harvested, histologically processed, and evaluated for bone area fraction occupancy (BAFO), vertical/horizontal ridge dimensions (VRD and HRD, respectively), and area of coronal soft tissue infiltration.Results: BAFO was statistically lower for the control group in comparison to all treatment groups. Defects treatedwith Bio-Oss® were not statistically different then defects treated solely with L-PRF. Collapsed across all groups,L-PRF exhibited higher degrees of BAFO than groups without L-PRF. Defects filled with Bio-Oss® and Bio-Oss®with L-PRF demonstrated greater maintenance of VRD relative to the control group. Collapsed across all groups,Bio-Oss® maintained the VRD and resulted in less area of coronal soft tissue infiltration compared to the emptydefect. Soft tissue infiltration observed at the coronal area was not statistically different among defects filled withL-PRF, Bio-Oss®, and Bio-Oss® with L-PRF.Conclusions: Inclusion of L-PRF to particulate xenograft did not promote additional bone heading at 6 weeks invivo. ... (AU)